- Specifications: ASTM A/ASME SA213/A249/A269/A312/A358 CL. I to V ASTM A789/A790
- Sizes (Seamless): 1/2" NB - 24" NB
- Sizes (ERW):1/2" NB - 24" NB
- Sizes (EFW): 6" NB - 100" NB
- Wall Thickness available:Schedule 5S - Schedule XXS (heavier on request)
- Other Materials Testing:NACE MR0175, H2 SERVICE, OXYGEN SERVICE, CRYO SERVICE, etc.
- Dimensions:All Pipes is manufactured and inspected/tested to the relevant standards including ASTM, ASME and API etc.
ASTM |
A312, A376,A358, A269, A249, A403, A182, A351 |
ASME |
SA312, SA376, Pressure SA358,SA269, SA249,SA403, SA182, SA351 |
Chemical Composition |
310 |
310S |
Carbon |
0.25 max |
0.08 max |
Manganese |
2.00 max |
2.00 max |
Silicon |
1.50 max |
1.50 max |
Phosphorus |
0.045 max |
0.045 max |
Sulphur |
0.030 max |
0.030 max |
Chromium |
24.00 - 26.00 |
24.00 - 26.00 |
Nickel |
19.00 - 22.00 |
19.00 - 22.00 |
Mechanical Properties |
310/ 310S |
Grade 0.2 % Proof Stress MPa (min) |
205 |
Tensile Strength MPa (min) |
520 |
Elongation % (min) |
40 |
Hardness (HV) (max) |
225 |
Properties |
at |
Value |
Unit |
Density |
|
8,000 |
Kg/m3 |
Electrical Conductivity |
25°C |
1.25 |
%IACS |
Electrical Resistivity |
25°C |
0.78 |
Micro ohm.m |
Modulus of Elasticity |
20°C |
200 |
GPa |
Shear Modulus |
20°C |
77 |
GPa |
Poisson's Ratio |
20°C |
0.30 |
|
Melting Rnage |
|
1400-1450 |
°C |
Specific Heat |
|
500 |
J/kg.°C |
Relative Magnetic Permeability |
|
1.02 |
|
Thermal Conductivity |
100°C |
14.2 |
W/m.°C |
Coefficient of Expansion |
0-100°C |
15.9 |
/°C |
|
0-315°C |
16.2 |
/°C |
|
0-540°C |
17.0 |
/°C |
STAINLESS STEEL SS 310 |
|
|---|---|
AISI |
310 |
UNS |
S31000 |
Werkstoff Nr. |
1.4841 |
NB SIZES |
SCH 5 | SCH 10 | SCH 40 | SCH 80 | SCH 160 |
|---|---|---|---|---|---|
1/8″ |
√ |
√ |
√ |
√ |
√ |
1/4″ |
√ |
√ |
√ |
√ |
√ |
3/8″ |
√ |
√ |
√ |
√ |
√ |
1/2″ |
√ |
√ |
√ |
√ |
√ |
3/4″ |
√ |
√ |
√ |
√ |
√ |
1″ |
√ |
√ |
√ |
√ |
√ |
1 1/4″ |
√ |
√ |
√ |
√ |
√ |
1 1/2″ |
√ |
√ |
√ |
√ |
√ |
2″ |
√ |
√ |
√ |
√ |
√ |
2 1/2″ |
√ |
√ |
√ |
√ |
√ |
3″ |
√ |
√ |
√ |
√ |
√ |
4″ |
√ |
√ |
√ |
√ |
√ |
5″ |
√ |
√ |
√ |
√ |
√ |
6″ |
√ |
√ |
√ |
√ |
√ |
- Manufacturer Test Certificate
- IBR Test Certificate (Form III-D)
- Laboratory Test Certificate from Govt. Approved Lab.
Polishing |
Victor Steel can polish nearly any stainless steel pipe item to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Stainless steel polished pipes can also be cut to size. |
Beveling |
Victor Steel can bevel stainless steel pipe to prepare for welding or other processes. |
Honing/Turning |
Victor Steel can hone pipe and tube, using a precision abrasion process in order to obtain a desired finish or close dimensional tolerance. |
Heatreating & Annealing |
Some grades of stainless steel pipe and tube can be heatreated to change the mechanical properties. Precipitation Hardening Stainless Steels such as 17-4PH can be heatreated. 410 stainless steel plate can also be heatreated. In some cases, secondary annealing 300 series stainless steel may be required depending on the application |
Positive Material Identification (PMI) |
Victor Steel can perform PMI testing in house for most stainless steel grades, or we can work with independent labs to complete PMI in order to meet customer specifications. |
UT Testing |
In some cases, UT testing of the stainless steel pipe and tueb may be required. We can assist you with this requirement. |